A bifunctional MnOx@PTFE catalytic membrane for efficient low temperature NOx-SCR and dust removal

Shasha Feng; Mengdi Zhou; Feng Han; Zhaoxiang Zhong; Weihong Xing

doi:10.1016/j.cjche.2019.11.014

Your Location：

Home >

Browse articles >

A bifunctional MnO_x@PTFE catalytic membrane for efficient low temperature NO_x-SCR and dust removal

Separation Science and Engineering | Updated：2026-01-06

- A bifunctional MnO_x@PTFE catalytic membrane for efficient low temperature NO_x-SCR and dust removal
- A bifunctional MnO_x@PTFE catalytic membrane for efficient low temperature NO_x-SCR and dust removal
- 中国化学工程学报（英文版） 2020年28卷第5期页码：1260-1267
- Affiliations：
  
  1. State Key Laboratory of Materials-Oriented Chemical Engineering, National Engineering Research Center for Special Separation Membrane, Nanjing Tech University,Nanjing,China,210009
  2. Nanjing Industrial Technology Research Institute of Membrane Material Co. Ltd.,Nanjing,China,211100
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2019.11.014
  中图分类号：
- 纸质出版：2020
- Accepted：
Scan QR Code
Shasha Feng, Mengdi Zhou, Feng Han, 等. A bifunctional MnO_x@PTFE catalytic membrane for efficient low temperature NO_x-SCR and dust removal[J]. 中国化学工程学报（英文版）, 2020,28(5):1260-1267. DOI: 10.1016/j.cjche.2019.11.014.

@PTFE catalytic membrane for efficient low temperature NO
Shasha Feng, Mengdi Zhou, Feng Han, 等. A bifunctional MnO_x@PTFE catalytic membrane for efficient low temperature NO_x-SCR and dust removal[J]. 中国化学工程学报（英文版）, 2020,28(5):1260-1267. DOI: 10.1016/j.cjche.2019.11.014. DOI：

@PTFE catalytic membrane for efficient low temperature NO DOI： 10.1016/j.cjche.2019.11.014.

摘要

Abstract

Low-temperature selective catalytic reduction of NO

combined with dust removal technique due to its energy conservation characteristic has been attracted much attention for fume purification. In this work

the MnO

wrapped PTFE membrane with efficient dust removal and low-temperature NH

-SCR has been prepared with a facile route. MnO

with different crystal structures was uniformly grown around the PTFE fibrils through water bath. The flower-sphere-like MnO

@PTFE(O-MnO

@PTFE) and lamellar-interlaced ripple-like MnO

@PTFE(W-MnO

@PTFE) have large specific surface area which is favorable for enhancing catalytic performance. Also

the uniformly wrapped W-MnO

around the PTFE fibrils optimized the pore structure for ultrafine dust capture. The membrane can almost 100% reject particles that are smaller than 1.0 μm with a low filtration resistance. Meanwhile

W-MnO

@PTFE with more surface chemisorbed oxygen has the best NO conversion efficiency of 100% at a comparatively low and wide activit

y temperature window of 160-210℃

which is far to the thermal limitation of the PTFE. Therefore

this efficient and energy conserving membrane has a bright application prospects for tail gas treatment compared to the original treatment process.

关键词

Keywords

references

浏览量

126

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Effect of samarium doping on the activity and sulfur resistance of Ce/MnFeOx catalyst for low-temperature selective catalytic reduction of NOx by ammonia

Catalytically active membranes for esterification: A review

Low-temperature dry reforming of methane tuned by chemical speciations of active sites on the SiO2 and γ-Al2O3 supported Ni and Ni-Ce catalysts

Boosting low-temperature selective catalytic reduction of NO with NH3 of V2O5/TiO2 catalyst via B-doping

Insight into SO2 poisoning and regeneration of one-pot synthesized Cu-SSZ-13 catalyst for selective reduction of NOx by NH3