Relationship between pore structure and hydration activity of CaO from carbide slag

Junqiang Zhang; Shu Zhang; Mei Zhong; Zhi Wang; Guoyu Qian; Junhao Liu; Xuzhong Gong

doi:10.1016/j.cjche.2019.02.024

Your Location：

Home >

Browse articles >

Relationship between pore structure and hydration activity of CaO from carbide slag

Energy, Resources and Environmental Technology | Updated：2026-01-06

- Relationship between pore structure and hydration activity of CaO from carbide slag
- Relationship between pore structure and hydration activity of CaO from carbide slag
- 中国化学工程学报（英文版） 2019年27卷第11期页码：2771-2782
- Affiliations：
  
  1. Key Laboratory of Green Process and Engineering, National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, Institute of Process Engineering, Chinese Academy of Sciences,Beijing,China,100190
  2. College of Materials Science and Engineering, Nanjing Forestry University,Nanjing,China,210037
  3. Key Laboratory of Coal Clean Conversion & Chemical Engineering Process(Xinjiang Uyghur Autonomous Region), College of Chemistry and Chemical Engineering, Xinjiang University,Urumqi,China,830046
  4. University of Chinese Academy of Sciences,Beijing,China,100190
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2019.02.024
  中图分类号：
- 纸质出版：2019
- Accepted：
Scan QR Code
Junqiang Zhang, Shu Zhang, Mei Zhong, 等. Relationship between pore structure and hydration activity of CaO from carbide slag[J]. 中国化学工程学报（英文版）, 2019,27(11):2771-2782.

Junqiang Zhang, Shu Zhang, Mei Zhong, Zhi Wang, Guoyu Qian, Junhao Liu, Xuzhong Gong. Relationship between pore structure and hydration activity of CaO from carbide slag[J]. Chinese Journal of Chemical Engineering, 2019, 27(11): 2771-2782.
Junqiang Zhang, Shu Zhang, Mei Zhong, 等. Relationship between pore structure and hydration activity of CaO from carbide slag[J]. 中国化学工程学报（英文版）, 2019,27(11):2771-2782. DOI： 10.1016/j.cjche.2019.02.024.

Junqiang Zhang, Shu Zhang, Mei Zhong, Zhi Wang, Guoyu Qian, Junhao Liu, Xuzhong Gong. Relationship between pore structure and hydration activity of CaO from carbide slag[J]. Chinese Journal of Chemical Engineering, 2019, 27(11): 2771-2782. DOI： 10.1016/j.cjche.2019.02.024.

摘要

Abstract

CaO needs to show high activity to be used as Ca-sorbent and slagging agent. Hydration activity is an important characteristic to evaluate the activity of CaO. In this study

carbide slag from polyvinyl chloride (PVC) industry was utilized as precursor for preparing high activity CaO. The roles of crystallite grain

average pore diameter (APD) and volume fraction of pore 200 nm in diameter (VF200) in hydration activity of CaO from carbide slag (CS-CaO) were respectively investigated. The hydrolysis kinetics model of CaO shows a three-dimensional spherically symmetric diffusion model (D4)

which suggests that hydration activity was mainly associated with APD and VF200 of CS-CaO with limited correlation to the crystal size. Specifically

the hydration activity of CS-CaO is increased with increasing VF200

while decreased with increasing APD. Under the invariable calcination temperature

the core-shell structure formed by the addition of graphite or CaCO

to CS effectively inhibits the sintering of CS-CaO and improves VF200. Consequently

the hydration activity of CS-CaO increased from 22.79℃·min

-1

to 27.19℃·min

-1

and to 29.27℃·min

-1

with a

ddition of 5% graphite or 5% CaCO

into carbide slag

respectively.

关键词

Keywords

references

浏览量

103

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Unraveling the methane decomposition mechanism on Fe-Ni-Ca-O composite catalysts: A combined density functional theory and microdynamic study

Ultrasonic-assisted rapid liquid-phase exfoliation of MFI-type zeolite nanoparticle aggregates

Reactivity study and kinetic evaluation of CuO-based oxygen carriers modified by three different ores in chemical looping with oxygen uncoupling (CLOU) process

Preparation and properties of a low-cost porous ceramic support from low-grade palygorskite clay and silicon-carbide with vanadium pentoxide additives

Investigation on the fabrication of lightweight aggregate with acid-leaching tailings of vanadium-bearing stone coal minerals and red mud