Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition

Guozhi Lü; Ting'an Zhang; Xiaofeng Zhu; Chaozhen Zheng; Yanxiu Wang; Weiguang Zhang; Zimu Zhang

doi:10.1016/j.cjche.2018.10.016

Your Location：

Home >

Browse articles >

Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition

Materials and Product Engineering | Updated：2026-01-06

- Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition
- Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition
- 中国化学工程学报（英文版） 2019年27卷第8期页码：1965-1972
- Affiliations：
  
  Key Laboratory of Ecological Metallurgy of Multi-metal Intergrown Ores of Ministry of Education, School of Metallurgy, Northeastern University,Shenyang,China,110819
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2018.10.016
  中图分类号：
- 纸质出版：2019
- Accepted：
Scan QR Code
Guozhi Lü, Ting'an Zhang, Xiaofeng Zhu, 等. Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition[J]. 中国化学工程学报（英文版）, 2019,27(8):1965-1972.

Guozhi Lü, Ting'an Zhang, Xiaofeng Zhu, Chaozhen Zheng, Yanxiu Wang, Weiguang Zhang, Zimu Zhang. Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition[J]. Chinese Journal of Chemical Engineering, 2019, 27(8): 1965-1972.
Guozhi Lü, Ting'an Zhang, Xiaofeng Zhu, 等. Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition[J]. 中国化学工程学报（英文版）, 2019,27(8):1965-1972. DOI： 10.1016/j.cjche.2018.10.016.

Guozhi Lü, Ting'an Zhang, Xiaofeng Zhu, Chaozhen Zheng, Yanxiu Wang, Weiguang Zhang, Zimu Zhang. Silicon saturation coefficient changes in hydrogarnets during the Bayer process with lime addition[J]. Chinese Journal of Chemical Engineering, 2019, 27(8): 1965-1972. DOI： 10.1016/j.cjche.2018.10.016.

摘要

Abstract

The relationship between the silicon saturation coefficient of hydrogarnets and Bayer reaction parameters was studied. The peak position

crystal plane spacing

and cell edge length of typical hydrogarnet patterns were calculated to find the key factors influencing the relationship. The results showed that the crystal face (420) is the optimal garnet growth direction during hydration and crystal growth along the faces (521) and (611) were not affected significantly by the varying experimental conditions. The reaction temperature significantly influenced the silicon saturation coefficient of hydrogarnets. The silicon saturation coefficient of hydrogarnets increased from 0.2 to about 1.0 in the temperature range of 30-270℃ and a rapid expansion process was observed in the temperature range of 120-150℃. Moreover

the reaction time

alumina concentration

and

C/S

were shown to be less important factors. Averaging the results obtained by the 3 methods was shown suitable for calculating the SiO

saturation coefficient of hydrogarnets. The calculated results of the Al

and SiO

contents matched the actual ones. However

the actual SiO

content was about 10% less than the calculated one for SiO

saturation coefficients higher than 1.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Non-isothermal decomposition kinetics of hydrogarnet in sodium carbonate solution

Synergistic Ba/Na promotion of BaFe2O4-derived catalysts for enhanced CO2 hydrogenation to light olefins

COS generation behavior during desulfurization for H2S over zeolite in simulated blast furnace gas

Dual-site engineering of Ga-modified HZSM-5 towards efficient propane aromatization

Enhanced mass transfer in flexible electrodes of open-pore cobalt disulfide nanosheets supported on sulfur-doped carbon fibers for efficient zinc-air batteries