Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics

Shenwen Fang; Manlin Wang; Zipei Xu; Lei Zhai; Xiujun Wang; Yan Xiong

doi:10.1016/j.cjche.2018.03.002

Your Location：

Home >

Browse articles >

Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics

Separation Science and Engineering | Updated：2026-01-06

- Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics
- Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics
- 中国化学工程学报（英文版） 2019年27卷第1期页码：130-135
- Affiliations：
  
  1. 2 Oil & Gas Applied Chemistry Key Laboratory of Sichuan Province,Chengdu,China,610500
  2. 3 Beijing Research Center of China National Offshore Oil Corporation,Beijing,China,100027
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2018.03.002
  中图分类号：
- 纸质出版：2019
- Accepted：
Scan QR Code
Shenwen Fang, Manlin Wang, Zipei Xu, 等. Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics[J]. 中国化学工程学报（英文版）, 2019,27(1):130-135.

Shenwen Fang, Manlin Wang, Zipei Xu, Lei Zhai, Xiujun Wang, Yan Xiong. Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics[J]. Chin.J.Chem.Eng., 2019, 27(1): 130-135.
Shenwen Fang, Manlin Wang, Zipei Xu, 等. Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics[J]. 中国化学工程学报（英文版）, 2019,27(1):130-135. DOI： 10.1016/j.cjche.2018.03.002.

Shenwen Fang, Manlin Wang, Zipei Xu, Lei Zhai, Xiujun Wang, Yan Xiong. Preparation of an amphoteric flocculant having both high polymer content and low viscosity and its polymerization kinetics[J]. Chin.J.Chem.Eng., 2019, 27(1): 130-135. DOI： 10.1016/j.cjche.2018.03.002.

摘要

Abstract

It is not easy for liquid cationic flocculant diallyldimethyl-ammonium chloride (DM) homopolymer to simultaneously exhibit both low viscosity and high polymer content

which limited its application in offshore oilfield. In this paper

sodium allylsulfonate (XS) and sodium formate were used in the aqueous solution polymerization of DM. An amphoteric flocculant (PDMXS) with the properties of high polymer content (about 55 wt%) and low viscosity (efflux time measured by an Apply 4 viscometer was less than 100 s) was prepared. The optimum reaction conditions were identified as follows:the mass ratio of XS/DM was 10 wt%

the concentration of sodium formate was 2000 mg·L

-1

reaction temperature was 55℃

the concentration of KPS was 0.5 wt% and the reaction time was 4 h. The polymerization kinetics was discussed. The results showed that R

∝[M

]

1.97

]

0.68

[CTA

]

0.71

and the apparent activation energy was 72.55 kJ·mol

-1

关键词

Keywords

references

浏览量

226

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Size-dependent decomposition behavior of limestone in fluidized bed calcination: Insights into fluidization, kinetics, and mechanisms

Understanding temperature-dependent degradation in proton exchange membrane water electrolyzer: The critical role of porous transport layer

Revealing critical factors in lignite-water interactions: From atomic to macroscopic

Nano-confinement construction of FeCo@NCNTs nanocomposite for pH-universal oxygen reduction catalysis and high-power Zn-air battery

A durable fluorine-free polyurethane-coated fabric with switchable super-wetting properties under mild pH conditions for controllable oil/water separation