Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission

Seyed Jalil Poormohammadian; Parviz Darvishi; Abdol Mohammad Ghalambor Dezfuli

doi:10.1016/j.cjche.2018.02.033

Your Location：

Home >

Browse articles >

Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission

Separation Science and Engineering | Updated：2026-01-06

- Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission
- Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission
- 中国化学工程学报（英文版） 2019年27卷第1期页码：100-109
- Affiliations：
  
  2 Physics Department, Shahid Chamran University of Ahvaz, Ahvaz,Iran
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2018.02.033
  中图分类号：
- 纸质出版：2019
- Accepted：
Scan QR Code
Seyed Jalil Poormohammadian, Parviz Darvishi, Abdol Mohammad Ghalambor Dezfuli. Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission[J]. 中国化学工程学报（英文版）, 2019,27(1):100-109.

Seyed Jalil Poormohammadian, Parviz Darvishi, Abdol Mohammad Ghalambor Dezfuli. Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission[J]. Chin.J.Chem.Eng., 2019, 27(1): 100-109.
Seyed Jalil Poormohammadian, Parviz Darvishi, Abdol Mohammad Ghalambor Dezfuli. Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission[J]. 中国化学工程学报（英文版）, 2019,27(1):100-109. DOI： 10.1016/j.cjche.2018.02.033.

Seyed Jalil Poormohammadian, Parviz Darvishi, Abdol Mohammad Ghalambor Dezfuli. Investigating the structural effect of electrospun nano-fibrous polymeric films on water vapor transmission[J]. Chin.J.Chem.Eng., 2019, 27(1): 100-109. DOI： 10.1016/j.cjche.2018.02.033.

摘要

Abstract

Electrospun polymers have many applications in the industry. However

the structure of these polymers has been less widely considered by researchers. In this work

the structural effect of electrospun and casted films of polyacrylonitrile (PAN) and polyvinylidene fluoride (PVDF) polymers on water vapor transmission were investigated. Sorption of water vapor was measured at 35

60 and 80℃ and different relative humidities. The diffusion coefficients were calculated based on mass changes of the polymer sample. The water vapor transmission rate (WVTR) was also measured at 35℃ and 90% relative humidity. The results indicated that electrospun nano-fibrous polymers (ESNPs) absorb much higher water vapor compared to non-porous casted polymers. The interaction of water molecules with mentioned polymers was investigated based on Flory-Huggins theory. The Flory-Huggins interaction parameter of electrospun films was less than casted films

suggesting much better interaction of water molecules with electrospun films. It was also found that electrospun films have anomalous kinetic behavior and do not obey the Fickian diffusion model. Finally

it was revealed that ESNPs show less resistance to water vapor transmission and they are good candidates for the applications of water vapor separation using membranes.

关键词

Keywords

references

浏览量

165

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Fabrication of Sb-based alloys/carbon nanofibers with uniform dispersion as anode material for high efficiency sodium storage

Application of different fiber structures and arrangements by electrospinning in triboelectric nanogenerators

Porous nanofibrous dressing enables mesenchymal stem cell spheroid formation and delivery to promote diabetic wound healing

Enhanced coalescence separation of oil-in-water emulsions using electrospun PVDF nanofibers

Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na2O-CaO-SiO2-H2O