Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO<sub>2</sub> foaming

Xin Xin; Yixin Guan; Shanjing Yao

doi:10.1016/j.cjche.2017.04.005

Your Location：

Home >

Browse articles >

Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming

Materials and Product Engineering | Updated：2026-01-06

- Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming
- Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming
- 中国化学工程学报（英文版） 2018年26卷第1期页码：207-212
- Affiliations：
  
  College of Chemical and Biological Engineering, Zhejiang University,Hangzhou,China,310027
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2017.04.005
  中图分类号：
- 纸质出版：2018
- Accepted：
Scan QR Code
Xin Xin, Yixin Guan, Shanjing Yao. Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming[J]. 中国化学工程学报（英文版）, 2018,26(1):207-212. DOI: 10.1016/j.cjche.2017.04.005.

foaming[J]. Chinese Journal of Chemical Engineering, 2018, 26(1): 207-212.
Xin Xin, Yixin Guan, Shanjing Yao. Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming[J]. 中国化学工程学报（英文版）, 2018,26(1):207-212. DOI: 10.1016/j.cjche.2017.04.005. DOI：

foaming[J]. Chinese Journal of Chemical Engineering, 2018, 26(1): 207-212. DOI： 10.1016/j.cjche.2017.04.005.

摘要

Abstract

Scaffolds with multimodal pore structure are essential to cells differentiation and proliferation in bone tissue engineering. Bi-/multi-modal porous PLGA/hydroxyapatite composite scaffolds were prepared by supercritical CO

foaming in which hydroxyapatite acted as heterogeneous nucleation agent. Bimodal porous scaffolds were prepared under certain conditions

i.e. hydroxyapatite addition of 5%

depressurization rate of 0.3 MPa·min

-1

soaking temperature of 55℃

and pressure of 9 MPa. And scaffolds presented specific structure of small pores (122 μm±66 μm) in the cellular walls of large pores (552 μm±127 μm). Furthermore

multimodal porous PLGA scaffolds with micro-pores (37 μm±11 μm) were obtained at low soaking pressure of 7.5 MPa. The interconnected porosity of scaffolds ranged from (52.53±2.69)% to (83.08±2.42)% by adjusting depressurization rate

while compression modulus satisfied the requirement of bone tissue engineering. Solvent-free CO

foaming method is promising to fabricate bi-/multi-modal porous scaffolds in one step

and bioactive particles for osteogenesis could serve as nucleation agents.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Effect of cobalt on the activity of nickel-based/magnesium-substituted hydroxyapatite catalysts for dry reforming of methane

Boron nitride silicone rubber composite foam with low dielectric and high thermal conductivity

Ionic liquid-assisted preparation of hydroxyapatite and its catalytic performance for decarboxylation of itaconic acid

Solubility of iron(III) and nickel(II) acetylacetonates in supercritical carbon dioxide

Foaming biocompatible and biodegradable PBAT/PLGA as fallopian tube stent using supercritical carbon dioxide

Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO2 foaming

Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO2 foaming

DOI：10.1016/j.cjche.2017.04.005

摘要

Abstract

关键词

Keywords

references

Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming

Bi-/multi-modal pore formation of PLGA/hydroxyapatite composite scaffolds by heterogeneous nucleation in supercritical CO₂ foaming