Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions

Xiaofeng Li; Xiaotao Sun; Yanting Zhang; Junliang Zhang; Pengchao Ren; Xiaozhen Liu; Tao Dou

doi:10.1016/j.cjche.2016.08.020

Your Location：

Home >

Browse articles >

Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions

Catalysis, Kinetics and Reaction Engineering | Updated：2026-01-06

- Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions
- Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions
- 中国化学工程学报（英文版） 2016年24卷第12期页码：1728-1734
- Affiliations：
  
  1. Research Institute of Special Chemicals, Taiyuan University of Technology,Taiyuan,China,030024
  2. Key Laboratory of Catalysis of CNPC, China University of Petroleum-Beijing, Changping,Beijing,China,102249
- Author bio：
- Funds：
- DOI：10.1016/j.cjche.2016.08.020
  中图分类号：
- 纸质出版：2016
- Accepted：
Scan QR Code
Xiaofeng Li, Xiaotao Sun, Yanting Zhang, 等. Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions[J]. 中国化学工程学报（英文版）, 2016,24(12):1728-1734.

Xiaofeng Li, Xiaotao Sun, Yanting Zhang, Junliang Zhang, Pengchao Ren, Xiaozhen Liu, Tao Dou. Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions[J]. , 2016, 24(12): 1728-1734.
Xiaofeng Li, Xiaotao Sun, Yanting Zhang, 等. Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions[J]. 中国化学工程学报（英文版）, 2016,24(12):1728-1734. DOI： 10.1016/j.cjche.2016.08.020.

Xiaofeng Li, Xiaotao Sun, Yanting Zhang, Junliang Zhang, Pengchao Ren, Xiaozhen Liu, Tao Dou. Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions[J]. , 2016, 24(12): 1728-1734. DOI： 10.1016/j.cjche.2016.08.020.

摘要

Abstract

EU-1 zeolites were sequentially treated with low-concentration sodium carbonate (Na

) and hydrochloric acid (HCl) solutions. The obtained samples were characterized by X-ray diffraction (XRD)

scanning electron microscopy (SEM)

adsorption/desorption

temperature programmed desorption of NH

(NH

-TPD)

solid state

Al nuclear magnetic resonance (

Al NMR)

and the catalytic performances of the treated samples were tested in the xylene isomerization reaction. The results showed that the external surface area and mesoporous volume of the sample sequentially treated with 0.05 mol·L

-1

and 0.1 mol·L

-1

HCl solutions reached 73.9 m

·g

-1

and 0.162 cm

·g

-1

respectively. The catalytic performances of EU-1 zeolites were significantly improved

that the activity of the probe reaction increased from 23.03% to 23.61% and the selectivity increased from 85.09% to 87.14% compared with those of parent sample. Furthermore

it was found that only amorphous silica and alumina species was dissolved during the post-tr

eatment process

but the framework structure and the acidic properties of EU-1 zeolite remained intact.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Controllable synthesis of Ni3S2/V3S4@NF-xF(x=0, 4, 8) catalysts for efficient hydrogen production in seawater and urea electrolyte

Synthesis of methyl diphenylmethane dicarbamate by methyl phenylcarbamate condensation catalyzed by NKC-9: Non-phosgene preparation of key precursors for diphenylmethane diisocyanate

CaO-stabilized tetragonal ZrO2 support for high-performance Ni—Fe alloy catalysts in dry reforming of methane

High activity in alkylation of benzene and 1-dodecene over MOR zeolite nanorods

Multiphysics coupling rule of semi-coke catalytic tar cracking