Al₂O₃-2SiO₂ Nanoparticles with Defined Al-Si Ratio:Processing Optimization and Conversion

MATERIALS AND PRODUCT ENGINEERING | Updated：2026-01-06

- Al₂O₃-2SiO₂ Nanoparticles with Defined Al-Si Ratio:Processing Optimization and Conversion
- Al₂O₃-2SiO₂ Nanoparticles with Defined Al-Si Ratio:Processing Optimization and Conversion
- 中国化学工程学报（英文版） 2012年20卷第2期页码：312-318
- Affiliations：
  
  1. School of Chemistry and Chemical Engineering, Guangxi University,Nanning,China,530004
  2. State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology,Beijing,China,100029
  3. College of Chemistry and Life Science, Guangxi Teachers Education University,Nanning,China,530001
- Author bio：
- Funds：
  
  Supported by the National Natural Science Foundation of China (50962002,50602006);Opening Funds of State Key Laboratory of Chemical Resource Engineering of Beijing University of Chemical Technology (201008)
- DOI：10.1016/S1004-9541(12)60393-0
  中图分类号：
- 纸质出版：2012
- Accepted：
Scan QR Code
郑广俭, 崔学民, 张伟鹏, 等. Al₂O₃-2SiO₂ Nanoparticles with Defined Al-Si Ratio:Processing Optimization and Conversion[J]. 中国化学工程学报（英文版）, 2012,20(2):312-318. DOI: 10.1016/S1004-9541(12)60393-0.

O
郑广俭, 崔学民, 张伟鹏, 等. Al₂O₃-2SiO₂ Nanoparticles with Defined Al-Si Ratio:Processing Optimization and Conversion[J]. 中国化学工程学报（英文版）, 2012,20(2):312-318. DOI: 10.1016/S1004-9541(12)60393-0. DOI：

O DOI： 10.1016/S1004-9541(12)60393-0.

摘要

Abstract

Attempts had been made to synthesize Al

-2SiO

nanopowders by sol-gel method with tetraethoxysilane (TEOS) and aluminum nitrate (ANN) as the starting materials.DTS

TEM

SEM and BET were employed to study the effects of process parameters on the size

specific surface area and structure (morphology) of powders.The alkali-activation reactivity of the powders was tested for manufacturing geopolymers and their hydrothermal reactions were performed for fabricating zeolites.The results show that the optimum process parameters and drying method for preparing Al

-2SiO

nanopowders are as follows:the molar ratio of water and ethanol to TEOS are 0:1 and 12:1 respectively at synthetic temperature of 50 ℃ and the drying method is azeotropic distillation with microwave drying.The average particle diameters of the powders were about 70 nm and the largest BET specific surface area was up to 669 m

·g

-1

.The compressive strength of the geopolymer and the calcium exchange capacity (by CaCO

) of NaA zeolite prepared with the powders reached to 29 MPa and 366 mg·g

-1

respectively.

关键词

Keywords

references

浏览量

1549

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

COS generation behavior during desulfurization for H2S over zeolite in simulated blast furnace gas

Synthesis of ZSM-5 zeolite from desiliconization solution of coal fly ash and adsorption properties of Pb2+ containing wastewater

Optimization of methanol distillation process using response surface methodology

Self-polymerization of dopamine on zinc oxide nanoparticles for enhanced corrosion resistance in epoxy-aluminum coatings

Effect of sodium zeolite mixed metal oxide catalysts on catalytic conversion of mixed-density plastic into carbon nanotubes and hydrogen fuel