Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding

W. H. Cheung; S. S. Y. Lau; S. Y. Leung; A. W. M. Ip; G. McKay

doi:10.1016/S1004-9541(11)60213-9

Your Location：

Home >

Browse articles >

Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding

香港科技大学化学与生物分子工程系戈登·麦凯教授退休纪念专刊 | Updated：2026-01-06

- Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding
- Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding
- 中国化学工程学报（英文版） 2012年20卷第3期页码：515-523
- Affiliations：
  
  1. Department of Chemical and Biomolecular Engineering, the Hong Kong University of Science and Technology,Hong Kong,China
  2. Scott Wilson Ltd, 38th Floor MetroPlaza Tower 1, Kwai Fong,Hong Kong,China
- Author bio：
- Funds：
- DOI：10.1016/S1004-9541(11)60213-9
  中图分类号：
- 纸质出版：2012
- Accepted：
Scan QR Code
W. H. Cheung, S. S. Y. Lau, S. Y. Leung, 等. Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding[J]. 中国化学工程学报（英文版）, 2012,20(3):515-523.

W. H. Cheung, S. S. Y. Lau, S. Y. Leung, A. W. M. Ip, G. McKay. Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding[J]. , 2012, 20(3): 515-523.
W. H. Cheung, S. S. Y. Lau, S. Y. Leung, 等. Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding[J]. 中国化学工程学报（英文版）, 2012,20(3):515-523. DOI： 10.1016/S1004-9541(11)60213-9.

W. H. Cheung, S. S. Y. Lau, S. Y. Leung, A. W. M. Ip, G. McKay. Characteristics of Chemical Modified Activated Carbons from Bamboo Scaffolding[J]. , 2012, 20(3): 515-523. DOI： 10.1016/S1004-9541(11)60213-9.

摘要

Abstract

In this study

bamboo scaffolding was used to produce activated carbon by carbonization at 600℃ and 900℃ with the purge of nitrogen.The 600℃ char was then further modified chemically by acids and alkalis by reflux for 6 hours.The produced chars were then characterized by nitrogen adsorption isotherm

He pyncometry

elemental analysis and Boehm titration.For most of the chemically modified carbons

the micropore surface areas and volumes have increased compared with the 600℃ char

while the mesopore surface areas and volumes slightly decreased

which may have been due to the dissolving of some of the permeated inorganic matter and oxidizing deposited carbon that blocks the pore openings.For the acidic modified carbons

larger amounts of acidic groups were present in the carbons after being activated by phosphoric acid

phosphoric acid further treated with 2 mol·L

-1

nitric acid

and calcium hydroxide.Although carbon treated with 2 mol·L

-1

and 5 mol·L

-1

nitric acid also produced high acidity

the surface areas and pore volumes were relatively low

due to the destruction of pores by nitric acid oxidation.The reduction of porosity may impair the adsorption capacity.

关键词

Keywords

references

浏览量

2711

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Error Analysis of Adsorption Isotherm Models for Acid Dyes onto Bamboo Derived Activated Carbon

Surface and Hydrogen Sorption Characteristics of Various Activated Carbons Developed from Rat Coal Mine (Zonguldak) and Anthracite

Removal of phenol via regulation of surface hybridization structure of activated carbon catalysts for persulfacte activation

Boosting high-energy-density zinc-ion capacitors with an ultra-stable redox mediator

Synergistic effect between nitrogen-doped sites and metal chloride for carbon supported extra-low mercury catalysts in acetylene hydrochlorination