Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials

宋伟明; 左春玲; 邓启刚

doi:10.1016/S1004-9541(09)60179-8

Your Location：

Home >

Browse articles >

Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials

Updated：2026-01-06

- Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials
- Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials
- 中国化学工程学报（英文版） 2011年19卷第1期页码：70-75
- Affiliations：
  
  College of Chemistry and Chemical Engineering of Qiqihar University,Qiqihar,China,161006
- Author bio：
- Funds：
- DOI：10.1016/S1004-9541(09)60179-8
  中图分类号：
- 纸质出版：2011
- Accepted：
Scan QR Code
宋伟明, 左春玲, 邓启刚. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. 中国化学工程学报（英文版）, 2011,19(1):70-75.

SONG Weiming, ZUO Chunling, DENG Qigang. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. , 2011, 19(1): 70-75.
宋伟明, 左春玲, 邓启刚. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. 中国化学工程学报（英文版）, 2011,19(1):70-75. DOI： 10.1016/S1004-9541(09)60179-8.

SONG Weiming, ZUO Chunling, DENG Qigang. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. , 2011, 19(1): 70-75. DOI： 10.1016/S1004-9541(09)60179-8.

摘要

Abstract

The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction(XRD)

adsorption-desorption studies

transmission electron microscopy(TEM)and surface morphology analysis(SEM)

surface acid(NH

-TPD)

reducibility properties(TPR)

X-ray energy dispersive spectrometer(EDS)and thermogravimetric analysis(TG/DTG).A l/La composite mesoporous material were synthesized with

(Al):

(La)=70:1.0

80℃ of reaction temperature

20 h of reaction time

12 h of crystallization time

650℃ of calcination temperature.The specific surface area of the sample is 273.90 m

·g

-1

with the average diameter 5.642 nm and pore volume 0.2354 cm

·g

-1

.The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined

and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650℃ had appropriate acid content

acid strength and better reducibility.

关键词

Keywords

references

浏览量

1272

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Dual-charged, non-swelling amine/carboxyl functionalized Fe—Mn mixed oxide composite for simultaneous removal of anionic and cationic azo dyes: Experimental and DFT studies

Efficiency and sustainability for removing organic pollutants in aqueous solution: An innovative composite material

Controllable synthesis of hydrogen-bonded organic framework encapsulated enzyme for continuous production of chiral hydroxybutyric acid in a two-stage cascade microreactor

Heteropolyacid hosted to nano-silica catalyst for the oxidation of methacrolein

Adsorption of ciprofloxacin on (Zn-Al) LDHs modified 3D reduced graphene oxide: Response surface methodology, adsorption equilibrium, kinetic and thermodynamic studies