Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure

肖新颜; 刘健飞

doi:10.1016/S1004-9541(08)60131-7

Your Location：

Home >

Browse articles >

Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure

Updated：2026-01-06

- Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure
- Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure
- 中国化学工程学报（英文版） 2008年16卷第4期页码：626-630
- Affiliations：
  
  School of Chemistry and Chemical Engineering, South China University of Technology,Guangzhou,China,510640
- Author bio：
- Funds：
- DOI：10.1016/S1004-9541(08)60131-7
  中图分类号：
- 纸质出版：2008
- Accepted：
Scan QR Code
肖新颜, 刘健飞. Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure[J]. 中国化学工程学报（英文版）, 2008,16(4):626-630.

XIAO Xinyan, LIU Jianfei. Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure[J]. , 2008, 16(4): 626-630.
肖新颜, 刘健飞. Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure[J]. 中国化学工程学报（英文版）, 2008,16(4):626-630. DOI： 10.1016/S1004-9541(08)60131-7.

XIAO Xinyan, LIU Jianfei. Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure[J]. , 2008, 16(4): 626-630. DOI： 10.1016/S1004-9541(08)60131-7.

摘要

Abstract

A fluorine-containing polyacrylate copolymer emulsion was synthesized by a seed emulsion polymerization method

in which methyl methacrylate (MMA) and butyl acrylate (BA) were used as main monomers and hexafluorobutyl methacrylate (HFMA) as fluorine-containing monomer. The structure and properties were characterized by Fourier transform infrared spectrum (FT-IR)

transmission electron microscopy (TEM)

particle size analysis

X-ray photoelectron spectroscopy (XPS)

contact angle (CA)

differential scanning calorimetry (DSC) and thermogravimetry (TG) analysis. The FTIR and TEM results showed that HFMA was effectively involved in the emulsion copolymerization

and the formed emulsion particles had a core-shell structure and a narrow particle size distribution. XPS and CA analysis revealed that a gradient concentration of fluorine existed in the depth profile of fluorine-containing emulsion film which was richer in fluorine and more hydrophobic in one side. DSC and TG analysis also showed that a clear core-shell structure existed in the fluorine-containing emulsion particles

and their film showed higher thermal stability than that of fluorine-free emulsion.

关键词

Keywords

references

浏览量

3303

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

A core–shell Ni/SiO2@TiO2 catalyst for highly selective one-step synthesis of 2-propylheptanol from n-pentanal

Functional monodisperse microspheres fabricated by solvothermal precipitation co-polymerization

ZrO2/PMMA Nanocomposites: Preparation and Its Dispersion in Polymer Matrix

Understanding temperature-dependent degradation in proton exchange membrane water electrolyzer: The critical role of porous transport layer

Research on the electrostatic spray characteristics of ethanol/n-butanol blended fuels