Browse articles >

Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes

Full Length Article | Updated：2026-01-06

- Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes
- Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes
- 中国化学工程学报（英文版） 2022年52卷第12期页码：56-65
- Affiliations：
  
  Key Laboratory for Ultrafine Materials of Ministry of Education, Shanghai Engineering Research Center of Hierarchical Nanomaterials, Frontiers Science Center for Materiobiology and Dynamic Chemistry, School of Materials Science and Engineering, East China University of Science & Technology,Shanghai,China,200237
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2022
- Accepted：
Scan QR Code
Jie Wang, Ling Zhang, Chunzhong Li. Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes[J]. 中国化学工程学报（英文版）, 2022,52(12):56-65.

Jie Wang, Ling Zhang, Chunzhong Li. Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes[J]. Chinese Journal of Chemical Engineering, 2022, 52(12): 56-65.
Jie Wang, Ling Zhang, Chunzhong Li. Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes[J]. 中国化学工程学报（英文版）, 2022,52(12):56-65. DOI：

Jie Wang, Ling Zhang, Chunzhong Li. Superhydrophobic and mechanically robust polysiloxane composite coatings containing modified silica nanoparticles and PS-grafted halloysite nanotubes[J]. Chinese Journal of Chemical Engineering, 2022, 52(12): 56-65. DOI：

摘要

Abstract

Excellent mechanical properties are the prerequisite for the application of superhydrophobic polymer coatings. However

significantly improving the mechanical properties without affecting other properties such as hydrophobicity is a huge challenge. In this study

a superhydrophobic coating with excellent mechanical properties was prepared by spraying a mixture of polysiloxane resins based on three siloxane monomers

hexadecyltrimethoxysilane (HDTMS) modified nano-SiO

particles (SiO

-HDTMS) and polystyrene-grafted halloysite nanotubes (HNTs-PS). SiO

-HDTMS dispersed homogeneously in polysiloxane coatings and the water contact angle of corresponding coating exceeding 150°

achieving superhydrophobicity. The SiO

-HDTMS/HNTs-PS/polysiloxane composite coatings showed excellent abrasion resistance with the water coating contact angle remaining above 150° after 90 abrasion cycles

indicating that HNTs-PS can significantly improve the mechanical properties of the coating without affecting the hydrophobic properties of the coating. The achieved coating also exhibited excellent antifouling and acid and alkali corrosion resistance. This

work provides a convenient and ecologically friendly method to prepare superhydrophobic polysiloxane composite coating with excellent mechanical properties

which is promising in the application of anti-fouling

anti-corrosion

and oil–water separation

etc

关键词

Keywords

references

浏览量

217

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

A soft sensing method for mechanical properties of hot-rolled strips based on improved co-training

Thermal aging and pyrolysis behavior of hyperbranched polymers grafted carbon fibers reinforced phthalonitrile/cyanate ester blend composites

Preparation and extrusion of ZSM-5 based on biomass templates for enhanced mechanical properties and catalytic pyrolysis performance

Properties evolutions during carbonization of carbon foam using lignin as sole precursor

Enhanced thermal conductivity and mechanical properties of boron nitride@polymethylacrylimide/epoxy composites with self-assembled stable three-dimensional network