Effect of boron addition on the MoO3/CeO2-Al2O3 catalyst in the sulfur-resistant methanation

Baowei Wang; Wenxia Yu; Weihan Wang; Zhenhua Li; Yan Xu; Xinbin M

Your Location：

Home >

Browse articles >

Effect of boron addition on the MoO₃/CeO₂-Al₂O₃ catalyst in the sulfur-resistant methanation

Catalysis, Kinetics and Reaction Engineering | Updated：2026-01-06

- Effect of boron addition on the MoO₃/CeO₂-Al₂O₃ catalyst in the sulfur-resistant methanation
- Effect of boron addition on the MoO₃/CeO₂-Al₂O₃ catalyst in the sulfur-resistant methanation
- 中国化学工程学报（英文版） 2018年26卷第3期页码：509-513
- Affiliations：
  
  Key Laboratory for Green Chemical Technology of the Ministry of Education, School of Chemical Engineering and Technology, Tianjin University,Tianjin,China,300072
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2018
- Accepted：
Scan QR Code
Baowei Wang, Wenxia Yu, Weihan Wang, 等. Effect of boron addition on the MoO₃/CeO₂-Al₂O₃ catalyst in the sulfur-resistant methanation[J]. 中国化学工程学报（英文版）, 2018,26(3):509-513.

/CeO
Baowei Wang, Wenxia Yu, Weihan Wang, 等. Effect of boron addition on the MoO₃/CeO₂-Al₂O₃ catalyst in the sulfur-resistant methanation[J]. 中国化学工程学报（英文版）, 2018,26(3):509-513. DOI：

/CeO DOI：

摘要

Abstract

The effect of boron on the performance of MoO

/CeO

-Al

catalysts

which were prepared with impregnation method

was investigated. The catalysts were characterized with N

adsorption-desorption

XRD

-TPR

and NH

-TPD

and were tested in sulfur-resistant methanation. The results indicated that the MoO

/CeO

-Al

catalysts modified by boron showed higher catalytic performance in sulfur-resistant methanation. The CO conversion increased from 47% to 62% with 0.5 wt% boron content. When the content of boron was under 0.5 wt%

the results suggested there was an increase in the amorphous form of MoO

caused by the generation of weak and intermediate acid sites

which had weakened the interaction between the active components and supports. While

the catalyst added 2.0 wt% boron showed the strong acid sites and the largest crystalline size resulting in the uneven distribution of ceria.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Rapid removal of boron from liquid media using wood-based functional materials modified with N-methyl-d-glucosamine

Preparation and application of nano dendritic polyurethane for high-efficiency boron adsorption

Boron separation by adsorption and flotation with Mg–Al-LDHs and SDBS from aqueous solution

Synthesis, characterization, and performance comparison of boron using adsorbents based on N-methyl-D-glucosamine

Promotion effect of Re additive on the bifunctional Ni catalysts for methanation coupling with water gas shift of biogas: Insights from activation energy