Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy

Kang Li; Wenfang Li; Guoge Zhang; Min Wang; Peng Tang

Your Location：

Home >

Browse articles >

Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy

材料与产品工程 | Updated：2026-01-06

- Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy
- Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy
- 中国化学工程学报（英文版） 2015年23卷第9期页码：1572-1578
- Affiliations：
  
  1. School of Materials Science and Engineering, South China University of Technology,Guangzhou,China,510641
  2. College of Mechanical Engineering, Guangdong Polytechnic Normal University,Guangzhou,China,510635
  3. School of Materials Science and Engineering, Guangxi University,Nanning,China,530004
- Author bio：
- Funds：
- DOI：
  中图分类号：
- 纸质出版：2015
- Accepted：
Scan QR Code
Kang Li, Wenfang Li, Guoge Zhang, 等. Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy[J]. 中国化学工程学报（英文版）, 2015,23(9):1572-1578.

Kang Li, Wenfang Li, Guoge Zhang, Min Wang, Peng Tang. Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy[J]. , 2015, 23(9): 1572-1578.
Kang Li, Wenfang Li, Guoge Zhang, 等. Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy[J]. 中国化学工程学报（英文版）, 2015,23(9):1572-1578. DOI：

Kang Li, Wenfang Li, Guoge Zhang, Min Wang, Peng Tang. Influence of surface etching pretreatment on PEO process of eutectic Al-Si alloy[J]. , 2015, 23(9): 1572-1578. DOI：

摘要

Abstract

To solve the problems generally encountered during the plasma electrolytic oxidation (PEO) of Al alloys with high Si content

a pretreatment of chemical etching was applied before the process. The influence of such pretreatment was studied by SEM

EDS and XRD. The pretreatment presents a significant effect on positive voltage at the beginning stage of PEO

leading to higher voltage over thewhole process. The difference between the positive voltages of non-etched and etched specimens decreases graduallywith the increase of processing time. The pretreatment exhibitsmuch less influence on the negative voltage. For the sample with surface pretreatment

the average growth rate of PEO coating is increased from 0.50 to 0.84 μm·min

-1

and the energy consumption is decreased from 6.30 to 4.36 kW·h·μm

-1

·m

-2

. At the same time

both mullite and amorphous SiO

contents are decreased in the coating.

关键词

Keywords

references

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

Multi-objective regulation in autohydrolysis process of corn stover by liquid hot water pretreatment

Pretreatment of Corn Stover Using Supercritical CO2 with Water-Ethanol as Co-solvent

Research on the electrostatic spray characteristics of ethanol/n-butanol blended fuels

CFD-PBM simulation of liquid-liquid dispersions in an industrial pulsed disc and doughnut column with directly measured breakup and coalescence kernels

A durable fluorine-free polyurethane-coated fabric with switchable super-wetting properties under mild pH conditions for controllable oil/water separation