Erosion corrosion performance of 6061 aluminum alloy in simulated sea water slurry was investigated under multi-phase jet impingement conditions. The main objective of the work is to study erosion-corrosion of a material with engineering application and mitigate it using eco- friendly green inhibitor. Experiments were performed with the sand concentration of 0.3% and 0.3 μm size. The effect of temperature and flow rate on the performance of inhibitor was explored. Electrochemical methods were adopted for erosion-corrosion measurements. Experiments revealed that starch could mitigate erosion-corrosion with a maximum reduction efficiency of 58% at temperature of 303 K and flow rate of 4 L·min

-1

. Inhibition efficiency decreased with increase in flowrate and temperature. EIS spectrum demonstrated that the corrosion process in the presence on inhibitor was both charge transfer and mass transfer controlled. A key role of hydrodynamics in the performance of corrosion inhibitor was confirmed by the present study.